LaserGloss Exterior

Main Specifications

Material:

Co-Extruded Impact Acrylic

Finish:

High Gloss

Sheet Size:

24" x 48" // 610mm x 1219mm

Engraving Depth:

.005" // 0.13mm

Attributes:

View Physical Properties

Usage:

Interior Signage

Exterior Signage

Personal Identification

Control Panels

Equipment ID Tags

Safety Signage

Recreational Signage

Industrial Signage/Tags

Trophies, Awards, & Plaques

Capabilities:

Saws

Drills

Shears

Laser Vector Cuts

Bevels

Heat Bendable

Screen Prints

Hot Stamps

Bonds

Permits Fine Engraving

Physical Properties

IZOD Impact Strength

Notched at 73°F (22.78°C)

Value:1.10ft lbs/in

ASTM Method:D-256

Tensile Strength

To break

Value:5,500 psi

ASTM Method:D-638

Elongation before break

Value:50%

ASTM Method:D-638

Flexural Strength

Load to stretch outer surface 5%

Value:10,300 psi

ASTM Method:D-790

Rockwell Hardness

Value:M45

ASTM Method:D-785

Specific Gravity

Value:1.15

ASTM Method:D-792

View Main Specifications

Deflection Temperature

D-792 Deflection Temperature Temperature at which material deflects .010" (.254mm) at 264 psi

Value:180°F (79.44°C)

ASTM Method:D-648

Coefficient of Thermal Expansion

Inch/inch/°F

Value:5.6 x 10^-5

ASTM Method:D-696

Vicat Softening Point

Temperature for needle to penetrate 1mm (90°F/hr, 2.2 lbs)

Value:208°F (97.78°C)

ASTM Method:D-1525

Additional Information

LaserGloss Exterior material softens sufficiently at approx. 180°F (82.22°C), which enables bending, should that be desired. It can also be drilled, sawed, sheared, and bonded to itself or other materials. Rowmark uses UV stable plastic resins and films in the manufacture of its products to prolong the useful life of the material when used in reasonable exterior conditions as such, Rowmark products will remain colorfast for 2+ years.

Electrically non-conductive, Insulative. Meets 10ˆ12 Ohms/square meter or higher in electrical resistivity, RoHS compliant (halogen-free), PVC-free, Formaldehyde and Phenol free and rated UL 94 HB. Material was judged as not contributing to the combustion of the base material.