Main Specifications
Material:
Microsurfaced Impact Acrylic
Finish:
High Gloss, Matte non-glare, Brushed, Patterned
Sheet Size:
24-1/8" x 48-3/4" // 613mm x 1238mm
23-1/2" x 49" // 597mm x 1245mm
Engraving Depth:
.003" // 0.08mm
Attributes:
Usage:
Interior Signage
Personal Identification
Safety Signage
Industrial Signage/Tags
Trophies, Awards, & Plaques
Capabilities:
Saws
Drills
Shears
Laser Vector Cuts
Bevels
Heat Bendable
Screen Prints
Hot Stamps
Bonds
Permits Fine Engraving
Physical Properties
IZOD Impact Strength
Notched at 73°F (22.78°C)
Value:1.10 ft lbs/in
ASTM Method:D-256
Tensile Strength
To break
Value:5,500 psi
ASTM Method:D-638
Elongation before break
Value:50%
ASTM Method:D-638
Flexural Strength
Load to stretch outer surface 5%
Value:10,300 psi
ASTM Method:D-790
Specific Gravity
LaserMark
Value:1.15
ASTM Method:D-792
Rockwell Hardness
LaserMark
Value:M45
ASTM Method:D-785
Deflection Temperature
Temperature at which material deflects .010" (.254mm) at 264 psi
Value:175°F (79.44°C)
ASTM Method:D-648
Coefficient of Thermal Expansion
Inch/inch/°F
Value:5.6 x 10^-5
ASTM Method:D-696
Vicat Softening Point
Temperature for needle to penetrate 1mm (90°F/hr, 2.2 lbs)
Value:208°F (97.78°C)
ASTM Method:D-1525
Temperature for needle to penetrate 1mm (90°F/hr, 11.0 lbs)
Value:187°F (86.11°C)
ASTM Method:D-1525
Additional Information
LASERMARK softens at about 200°F (93.33°C) sufficiently so that it can be bent as needed. It can be sawed, drilled and bonded, but not sheared.
The base material was tested for flammability by Underwriters Laboratories. The material is rated 94 HB on the UL 94 test.